Permanently doped polyaniline and method thereof

ABSTRACT

The present invention relates to an electrically conducting polymer, the water-insoluble polymer having essentially permanent self-doping properties, and the polymer comprises: 
     (a) electrically polymerized polyaniline in covalent combination with 
     (b) an organic dopant having at least one sulfonic acid functional group. The electrically conducting polymer-dopant is preferred wherein the organic dopant is selected from benzenesulfonic acid, toluenesulfonic acid, benzenesulfonyl chloride, dodecylbenzenesulfonic acid, poly(vinylsulfonic) acid, trifluoromethanesulfonic acid, 1-butanesulfonic acid, modified NAFION, 2,3,5-trichlorobenzenesulfonic acid, vinylphenylsulfonic acid, or the alkali metal salts thereof. In another aspect, the present invention discloses a method to produce a water-insoluble polyaniline in which an aromatic organic dopant is covalently bonded to the polyaniline, which method comprises (a) electropolymerizing aniline in an aqueous solvent which contains the organic dopant. These permanently doped polyanilines are useful as films for electric battery electrodes, and for electrochromic applications.

BACKGROUND OF INVENTION

Origin of Invention

The present invention is a continuation-in-part of pending U.S. Patent Application Ser. No. 238,571, filed Aug. 30, 1988, which is incorporated herein by reference.

FIELD OF INVENTION

The present invention relates to a permanently doped polyaniline and its method of production. More specifically, the present invention relates to a permanently doped polyaniline as a film and its production by the electropolymerization of a solution of aniline and an organic dopant, such as an organic sulfonate, and the use of the film in electrical transmission and storage, e.g. as an electrode in an advanced electrical storage battery.

DESCRIPTION OF RELATED ART

During the last five years, a great deal of effort has been expended to develop polyaniline-based rechargeable polymer batteries, especially in conjunction with a lithium anode in nonaqueous electrolytes. The doping rate of polyaniline is about twice that of any other conducting polymers, and the stability of polyaniline is probably the best. Recently, the first commercial, coin-shaped polyaniline/lithium battery suitable as a memory back-up power source was developed by T. Kita et al. for Bridgestone/Seiko. See "Properties of Polyaniline Secondary Battery," Abstract No. 24, 170th Electrochemical Society Meeting, San Diego, Calif., October 1986. Table 1 summarizes typical performance characteristics of three secondary battery systems (i.e. lead-acid, nickel-cadmium, and Bridgestone's new polyaniline battery).

The following references relate to Table 1:

A. G. MacDiarmid et al. (1986), Extended Abstracts, Vol. 86, Abstract #2, 170th Electrochemical Society Meeting, San Diego, Calif., October 19-24.

A. Kitani et al., (1986), Journal of the Electrochemical Society, Vol 133, #6, pp. 1069-1073.

N. Koura et al., Denki Kagaku, Vol. 55, #5, pp. 386-391.

                                      TABLE 1                                      __________________________________________________________________________     COMPARISON OF DIFFERENT POLYANILINE ELECTRODES                                               MacDiarmid                                                                            Kitani                                                                  and Yang                                                                              et al. Koura and Kijima                                                                             SRI                                                (1986) (1986) (1987)        (Preliminary data)                   __________________________________________________________________________     Polyaniline electrode                                                                        powder e.c. polymer                                                                          powder powder e.c. polymer                         Starting materials                                                                           aniline                                                                               0.1 M aniline                                                                         0.5 M aniline                                                                         0.5 M aniline                                                                         0.1 M aniline                                      (NH.sub.4).sub.2 S.sub.2 O.sub.8                                                      0.1 M H.sub.2 SO.sub.4                                                                0.1 M HC1                                                                             0.1 M H.sub.2 SO.sub.4                                                                1 M tosylate                         Preparation method                                                                           chemical                                                                              PC.sup.d /Pt                                                                          CP.sup.f /graph                                                                       CP.sup.f /graph                                                                       PC.sup.i /Pt                         Weight of polyaniline (g)                                                                    -0.04  (2 × 2 cm)                                                                      5?     5      -0.024                               Electrolyte   PC/LiCiO.sub.4                                                                        1 M ZnSO.sub.4                                                                        AlCl.sub.3 BPC.sup.g                                                                  0.5 M ZnSO.sub.4                                                                      1 M ZnSO.sub.4                                            (pH 4.6)             (pH 2.3)                             Anode (negative elec-                                                                        Li     Zn (beads)                                                                            A1     Zn sheet                                                                              Zn sheet                             trode)                                                                         Open-cell voltage (V)                                                                        3.3    -1.1   1.7    1.4    1.5                                  Short-circuit current (mA)                                                                   --     --     --     --     3.0                                  Capacity (Ah/kg)                                                                             147.7.sup.b                                                                           <108   130    100    -36                                  Capacity.sup.a (Ah/kg)                                                                       92.7   --     --     --     --                                   Power density (kW/kg)                                                                        --     --     --     --     0.2                                  Energy density (Wh/kg)                                                                       539.2.sup.a                                                                           <111   180    -140   -39                                  Energy density.sup.a (Wh/kg)                                                                 338.3  --     --     --     --                                   Coulomb efficiency (%)                                                                       --     100.sup.e                                                                             85-90.sup.h                                                                           -85.sup.i                                                                             -86.sup.k                            Cycle life (cycles)                                                                          --     <2000.sup.e                                                                           -60.sup.h                                                                             <60.sup.i                                                                             >400.sup.l                           Self-discharge rate                                                                          57     --     6      --     high                                 (%/month)                                                                      __________________________________________________________________________      .sup.a Including the weight of electrolyte.                                    .sup.b Discharge rate of 0.2 mA/cm.sup.2.                                      .sup.c At an average discharge voltage of 3.65 V.                              .sup.d Potential cycle (100 mV/s) for 1000 times between -0.2 and +0.8 V       vs. SCE.                                                                       .sup.e Cycled between 1.35 V and 0.75 V at a constant current density of       mA/cm.sup.2.                                                                   .sup.f Constant potential of 1 V vs. SCE for 72 hours using graphite           electrode.                                                                     .sup.g 2:1 mixture of AlCl.sub.3 and lbutylpyridinium chloride.                .sup.h At ±4 mA/cm.sup.2.                                                   .sup.i At ±2 mA/cm.sup.2.                                                    .sup.j Potential cycle (100 mV/g) for 4 hours between -0.2 V and +0.8 vs      SCE at 30° C.                                                           .sup.k Cycled between 1.35 V and 0.75 at ±10 mA/cm.sup.2.                   .sup.l At ±10 mA/cm.sup.2.                                            

The T. Kita/Bridgestone polyaniline battery offers attractive characteristics such as high operating voltage, good cycle life and low self-discharge rate. In addition, polyaniline batteries in general appear to be intrinsically superior to other existing secondary batteries because of potentially high charge capacity and high energy density (features not yet realized in the Bridgestone battery). Furthermore, although the polyaniline/lithium nonaqueous battery developed by Bridgestone/Seiko is said to exhibit excellent shelf-life, i.e. little self-discharge, there are difficulties associated with the use of a nonaqueous solvent (e.g. propylene carbonate) in conjunction with a lithium electrode in rechargeable batteries, including:

1. Low capacity (less than 0.004 Ah) and low current output (less than 5mA).

2. Corrosion is a problem: the lithium surface is gradually covered by some passive film such as Li₂ CO₃ during the repeated cycling of charge and discharge.

3. The high cathodic potential of the Li/Li+ couple often causes solvent decomposition.

Japanese patent application [JP 62/12073] by Hitachi/Showa Denko discloses the use of tosylate in conjunction with polyaniline. It is apparent that the two batteries are quite different in terms of their fundamental principles. The Hitachi/Showa Denko battery is essentially a conventional polyaniline/Li nonaqueous battery, in which anions such as ClO₄ - are dopants in the positive polyaniline electrode. The tosylate is used merely as a sacrificial material (Anions with a larger ionic radius, such as tosylate, are added during electropolymerization of aniline. The grown polyaniline film is rinsed thoroughly with water to get rid of the added anions, leaving the polyaniline with a high microporous channel structure through which small anions, e.g. ClO-₄, can easily diffuse in and out).

Organic conducting polymers such as polypyrrole (PPy), polythiophene (PTP), polyaniline (PAn or PAN) and their derivatives are gaining in popularity for potential use in optical, electronic and electrochemical devices. See, for example, F. Garnier et al., Journal of Electroanalytical Chemistry (1983), Vol. 148, p. 299; H. Kaezuka, et al., Journal of Applied Physics (1983), Vol. 54, p. 2511; and A. Mohammadi et al., Journal of the Electrochemical Society (1986), Vol. 133, p. 947.

A major disadvantage of these electrically conducting polymers in any configuration is that they usually have poor mechanical properties. See, for example, O. Niwa, et al., Journal of the Chemical Society (1984), p. 817; S. E. Lindsey, et al., "Synthetic Methods," (1984/1985), Vol 10, p. 67; F.R.F. Fan, et al., Journal of the Electrochemical Society, Vol 133, p. 301; and R. M. Penner, et al., Journal of the Electrochemical Society (1986), Vol. 133, p. 310.

Several approaches may be useful to improve the physical and mechanical properties of the conducting polymers. For instance, the polymerization of pyrrole in thick electroactive polymer networks such as poly(vinylchloride), poly(vinyl alcohol), NAFION and NAFION®, a trademark of the E.I. DuPont Co., Inc. of Wilmington, Del., for a perfluorinated sulfonic acid material and membrane, and NAFION®-impregnated GORE-TEX^(R), where GORE-TEX^(R) is a trademark of W. F. Gore and Associates of Elkton, Md., for a porous polytetrafluoroethylene material. has been reported in the literature.

T. Harai, et al., Journal of the Electrochemical Society (1988), Vol. 135 (#5), p. 1132-1137 reported that the anodic polymerization of pyrrole, 3-methylthiophene and aniline at NAFION ®-coated electrodes gives electrically conducting polyaniline (NAFION) composite films. These composites show an improvement of the polypyrrole electrochromic response and by the efficient utilization of stored charge by the composite film electrodes.

All of the disclosure in the references cited herein are incorporated herein by reference.

These references do not teach or suggest a permanently doped polyaniline for use as a secondary battery as is described in the present invention.

SUMMARY OF THE INVENTION

The present invention relates to an electrically conducting polymer having essentially permanent self-doping properties, said polymer comprising:

(a) electrically polymerized polyaniline matrix chemically combined with

(b) an organic dopant having at least one sulfonic acid functional group.

In a preferred embodiment of the present invention, the electrically conducting polymer combination, the organic dopant is independently selected from benzenesulfonic acid, toluenesulfonic acid, benzenesulfonyl chloride, 2-ethylbenzenesulfonic acid, vinyl sulfonic acid, dodecylbenzenesulfonic acid, poly(vinylsulfonic) acid, trifluoromethanesulfonic acid, 1-butanesulfonic acid, modified NAFION ® solution, 2,3,5-trichlorobenzenesulfonic acid or vinylphenylsulfonic acid or the alkali metal salts thereof.

In another embodiment, the present invention is a method to produce a water-insoluble polyaniline to which an organic dopant is chemically bound to the polyaniline, which method comprises:

(a) electropolymerizing aniline in an aqueous solvent which contains the organic dopant

Additional embodiments are found in the description below and in the claims.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 shows a schematic diagram of the rechargeable polyaniline battery.

FIG. 2A shows the resistance of various conventional polyaniline films as a function of gate potential, V_(G), between two adjacent micro-electrodes.

FIG. 2B shows the resistance of permanently doped polyaniline-tosylate films as a function of gate potential, V_(G), between two adjacent micro-electrodes.

FIG. 3 over all shows typical cyclic voltammograms of aniline during polymerization and grown polyaniline films in aqueous solution FIG. 3A shows aniline/sulfuric acid during polymerization on a 3-dimensional electrode substrate (e.g., fat posts). FIG. 3B shows aniline/tosylate during polymerization on a 3-dimensional fat posts electrode. FIG. 3C shows polyaniline/ sulfuric acid film production in aqueous 0.5M sodium sulfate at pH 1.2. FIG. 3 D shows polyaniline/tosylate film electropolymerization in aqueous 0.5M sodium sulfate at pH 1.2.

FIG. 4 shows an X-ray fluorescence spectroscopic analysis (EDAX) spectrum of the polyaniline/tosylate.

FIG. 5 shows a scanning electron micrograph (SEM) of the polyaniline/tosylate.

FIG. 6 shows a comparison of the long-term charge discharge curves (cell voltage versus time) at ± 10 milliamperes/centimeter2 in 1M zinc sulfate at pH 2.3. FIG. 6A self-doped polyaniline/tosylate (1M in tosylate and 0.1 M aniline on a 3-dimensional fat post electrode with a zinc-dispersed NAFION ® film as an anode. FIG. 6B shows a conventional (undoped) polyaniline film (0.1M sulfuric acid and 0.1 M aniline) on a 3-dimensional fat COCO electrode with a zinc sheet anode.

FIG. 7 shows the coulomb efficiency and capacity of various polyaniline electrodes as a function of charge-discharge current density in 1M zinc sulfate. FIG. 7A shows the coulomb efficiency of the half cell battery. FIG. 7B shows the capacity when zinc is used as an anode.

FIG. 8 shows the resistance of various polyaniline films as a function of gate potential, V_(G), between two adjacent platinum electrodes.

FIG. 9 shows typical cyclic voltammograms of polyaniline/benzenesulfonic acid. FIG. 9A shows the electropolymerization of 0.1 M aniline and 1M benzene-sulfonic acid. FIG. 9B shows the electropolymerization of polyaniline/benzenesulfonic acid film in aqueous 0.5M sodium sulfate at pH 1.2.

FIG. 10 shows scanning electron micrographs of polyaniline/benzenesulfonic acid film. FIG. 10A is at the 200 micrometer scale. FIG. 10B is at the 40 micrometer scale.

FIG. 11 shows a graph of the resistance of polyaniline/benzenesulfonic acid as a function of gate potential, V_(G), (in volts versus SCE) between two adjacent micro-electrodes.

FIGS. 12 a and b shows graphs of the coulomb efficiency and capacity of polyaniline/benesulfonic acid electrode as a function of charge-discharge current density in 1M sulfuric acid.

FIG. 13 shows typical cyclic voltammograms of polyaniline/polyvinylsulfonic acid. FIG. 13A is the voltammogram during polymerization 0.1 M aniline and 12.5% polyvinylsulfonic acid. FIG. 13A is the voltagram for polyaniline/polyvinylsulfonic acid film in aqueous 0.5M sodium sulfate at pH 1.2.

FIG. 14 shows scanning electron micrographs of polyaniline/polyvinylsulfonic acid film. FIG. 14A is a 200 micrometers. FIG. 14B is at 40 micrometers.

FIG. 15 is a graph of the resistance in ohms of polyaniline/polyvinylsulfonic acid as a function of gate potential, V_(G), (in volts versus SCE), between two adjacent micro-electrodes.

FIG. 16 shows four plots of coulomb efficiency and capacity of various polyaniline/polyvinylsulfonic acid electrodes as a function of charge-discharge currently density in 1M sulfuric acid. FIG. 16A is coulomb efficiency of a various half cell batteries. FIG. 16B is the capacity of various half cell batteries. FIG. 16C is coulomb efficiency of zinc as an anode. FIG. 16D is the capacity of zinc as an anode.

FIG. 17 shows typical cyclic voltammograms of polyaniline/trifluoromethanesulfonic acid. FIG. 17A is the voltammogram during polymerization in 0.1 M aniline and 1M trifluoromethanesulfonic acid. FIG. 17B is the cyclic voltammogram of polyaniline/trifluoromethanesulfonic acid film in aqueous 0.5M sulfuric acid at pH 1.2.

FIG. 18 are photographs of scanning electron micrographs of polyaniline/trifluoromethanesulfonic acid film. FIG. 18A is at 200 micrometers. FIG. 18B is at 40 micrometers.

FIG. 19 shows a plot of the resistance in ohms of polyaniline/trifluoromethanesulfonic acid as a function of gate potential V_(G), between two adjacent micro-electrodes.

FIG. 20 shows graphs of coulomb efficiency and capacity of various polyaniline/trifluoromethanesulfonic acid electrodes as a function of charge-discharge current in 2M zinc sulfate. FIG. 20A is a graph of the coulomb efficiency, half cell battery. FIG. 20B is a graph of the capacity, half cell battery. FIG. 20C is a graph of the coulomb efficiency, zinc as an electrode. FIG. 20D is a graph of the capacity having zinc as anode.

FIGS. 21a, b, c, d shows a plot of accelerated stability tests for four self-doped polyaniline electrodes, PAN/Bs, PAN/PVSA, PAN/Ts, and PAN/TFMSA.

FIGS. 22a and b shows a graph of long term charge/discharge curves at+or -15mA cm² in 1M ZnSO₄ (pH 2.3) with a zinc anode.

FIG. 23 shows a graph of the open circuit voltage as a function of time for self-doped polyaniline-zinc batteries.

FIG. 24 shows photographs of the surface morphology of two self-doped polyanilines PAN/TFMSA and PAN/Ts at 200μm and 40μm.

FIG. 25 shows photographs of the surface morphology of two self-doped polyanilnes PAN/PVSA and PAN/Bs at 200μm and 40μm.

DETAILED DESCRIPTION OF THE INVENTION AND PREFERRED EMBODIMENTS Definitions

As used herein:

"Aliphatic dopant" refers to aliphatic, unsaturated, cyclic, bridged and/or fluorine substituted organic compounds having from 1 to 20 carbon atoms, preferably having from to 12 carbon atoms, and more preferably having from 1 to 6 carbon atoms.

"Aromatic dopant" refers to those organic compounds which have a 5, 6, or 7 membered aromatic (e.g., benzene, toluene, naphatalene, chlorobenzene, nitrobenzene, and the like) or heteroaromatic (e.g., pyrrole, pyridine, quinoline and the like) sulfonic acid compounds. Aromatic compounds are preferred.

"Organic dopant" refers to aliphatic unsaturated, cyclic, bridged, aromatic heteroaromatic organic sulfonic acids (--SO₃ H), acid chlorides (--SO₂ Cl), or alkali salts (--SO₃ M, wherein M is, for example, sodium or potassium). Organic means that at least one carbon atom is present, e.g. trifluoromethanesulfonic acid.

The present invention is an almost all polymer solid state battery comprising a permanently-doped polyaniline polymeric cathode (e.g., polyaniline/dopant), an optional solid polymer (e.g. NAFION ® film) and a zinc anode (e.g., zinc microparticles dispersed in a NAFION film). FIG. 1 schematically represents the rechargeable polymer battery. A major advantage of using a permanently-doped polyaniline cathode is that it requires only the hydrogen ions be incorporated and expelled during the discharge/charge cycle, because the negative charge sites, i.e., anions are designed to be immobilized in the polyaniline polymer matrix.

In the discussion below, the polyaniline-dopant copolymer produced has a number of different forms. In a preferred embodiment, a substantially smooth polymer is formed which is useful in electrical transmission and/or storage, e.g., as a battery electrode. In another embodiment, a "flakey" type of product is obtained. This flakey material is useful to conduct or store electricity after it is pressed into a wire or pellet form using heat and/or pressure methods which are conventional in the art.

P-Toluenesulfonic Acid Dopant and Polyaniline

Comparison of Self-Doped Polvaniline/Tosylate (Toluenesulfonic Acid) and Conventional Polyaniline made with Sulfuric Acid--The polyaniline/tosylate polymer is synthesized electrochemically in an aqueous solution containing about 0.1 M aniline and about 1 M tosylate (p-toluenesulfonic acid), which produces a pH=0.65, using a potential-cycling method, from -0.2 V to +0.8 V at a rate of 0.1 V/second for 5.5 hours. FIG. 2A compares the resistance of various conventional polyaniline films as a function of the applied potential measured using an interdigitated microelectrode array. FIG. 2B has the surprising feature in that the permanently doped polyaniline/tosylate polymer is much more conductive (of the order of about 1 to 100 S/cm). The residual electrical proeprties are seen in FIG. 2B in the region of about 0.6 to 1.3 volts. FIG. 3B shows a typical cyclic voltammo-gram (CV) during the polymerization. Unlike the relatively featureless polymerization CV curve of a polyaniline made from 0.1M aniline and 0.1M H₂ SO₄, shown in FIG. 3A, polyaniline/tosylate shows an additional redox peak about 0.2 V, which is due to the oxidation of polyaniline by the incorporation of tosylate, i.e. SO₃ -group. The presence of the sulfonic groups (SO₃ -) within the polyaniline/tosylate polymer system was also confirmed by an EDAX analysis, which showed the presence of a large amount of elemental sulfur (see FIG. 4). FIGS. 3C and 3D compare cyclic voltammograms of 0.5 M Na₂ SO₄ of the two grown films. While the polyaniline/tosylate system shows a mostly featureless CV curve, however, with a large double-layer charging current (more than 50 mA/cm²) (FIG. 3D), the polyaniline/H₂ SO₄ shows an additional peak around 0.3 V that is due to the conventional anion doping (FIG. 3C). FIG. 5 shows the morphology of the self-doped polyaniline/tosylate polymer. The surface exhibits an ultrafine microstructure with a highly electroactive surface, which accounts for the observed high electrochemical capacitance.

The polyaniline/tosylate film is chemically more stable than conventionally made polyanilines. Indeed, FIG. 6A demonstrates that the Zn polyaniline/tosylate polymer battery shows no sign of degradation after 400 charge/discharge cycles at ±10 mA/cm², while the conventional polyaniline made in H₂ SO₄ using the same potential-cycling method shows a degraded performance after only 50 cycles in about 6,000 seconds, FIG. 6B.

The charge/discharge reaction of the polyaniline/tosylate polymer electrode may be written as: ##STR1## where P denotes polyaniline. In the mechanism proposed in Eq. (1), only small H⁺ ions are mobile, because the mechanism assumes that tosylates containing SO₃ - groups are immobilized in the polymer chains. This immobilization results in a more reversible electrode kinetics, better chemical stability, and a higher energy density than the conventional polyaniline electrodes, in which anions must diffuse in and out during a charge/discharge process, imparting some mechanical stress to the polymer film. Moreover, the mechanism of Eq. (1) should allow the use of a solid polymer electrolyte, e.g. Nafion, which provides better chemical stability, less resistance (especially when a thin film is used), and is easier to handle than the conventional organic and aqueous electrolytes.

Table 1 above summarizes typical performance characteristics of different polyaniline electrodes reported in the literature as well as the present polyaniline/tosylate polymer. It is misleading, however, to directly compare data from different laboratories because there may be many differences in fabrications, operations, and evaluation of batteries (for example, the weight of the present polyaniline electrode includes the weight of a considerable amount of water because the polyaniline is not removed from the electrode substrate).

    ______________________________________                                         Exhibit 1                                                                      DEFINITION OF SOME IMPORTANT                                                   BATTERY PARAMETERS                                                             ______________________________________                                         (a) Dopant Concentration y (%)                                                  ##STR2##                                                                      where W (mg) is the weight of a polyaniline electrode, Q                       (coulomb) is the total charge involved, M (g/mol) is the                       molecular weight (92 for C.sub.6 H.sub.4 NH), and F (coulomb/mol) is           Faraday's constant (9.65 × 10.sup.4).                                    (b)  Power Density P.sub.max  (kW/kg)                                          P.sub.max  = V.sub.oc  × I.sub.ac /(4 × W × 10.sup.-3)       where V.sub.oc  is open-circuit cell voltage and I.sub.ac  is short-circui     current.                                                                       (c) Energy Density, E.sub.out  (Wh/kg); Capacity Q.sub.total,out               (Ah/kg)                                                                        E.sub.out  = V.sub.d  × Q.sub.total,out /W × 10.sup.-3             where V.sub.d  is the cell voltage during discharge. The charging input        energy is given by:                                                            E.sub.in  = V.sub.c  × Q.sub.total,in /W × 10.sup.-3               where V.sub. c  is the cell voltage during charge.                             (d) Energy Efficiency (η.sub.Wh); Coulomb Efficiency (η.sub.Ah)        Energy efficiency:  η.sub.Wh  = E.sub.out /E.sub.in                        Coulomb efficiency: η.sub.Ah  = Q.sub.total,out /Q.sub.total,in            ______________________________________                                    

Some important battery performance parameters are defined in Exhibit 1. The data indicate that the performance (e.g. capacity and energy density) of the polyaniline-polymer/Zn battery is already comparable to that of a typical lead-acid battery. However, in comparison with batteries made using polyaniline/H₂ SO₄ films, it is clear that the performance of the polyaniline/tosylate/zinc battery is nearly comparable in terms of capacity, energy density, and self-discharge rate. The relatively low energy density and capacity observed with the polyaniline/tosylate is attributed to the relatively heavy weight of tosylate (FW 172).

POLYMERIZATION CONDITIONS FOR THE POLYANILINE/TOSYLATE 1. Solution Temperature During Polymerization

The effect of the solution temperature during polymerization (20°, 30°, and 40° C.) is examined. The results are summarized in Table 2. For comparison, the performance of the conventional polyaniline polymer electrode made with H₂ SO₄ is presented.

As the solution temperature increases, the kinetics of the electrochemical polymerization for the aniline/tosylate becomes faster, and less time is required to grow the films. However, increasing the solution temperature also encourages the chemical reaction, which competes with the electrochemical polymerization reaction, to form an insulating film. When the solution temperature is 40° C., a very flaky polymer film is formed, PAN 85, which results in a degraded battery performance. Among the three polyaniline/tosylate polymer electrodes studied, the best result in terms of change capacity is obtained when the solution temperature is room temperature, i.e. 20° C. (PAN 83); however, the coulomb efficiency (about 60 percent) is poorer than that of the conventional polyaniline electrode at the low current density of ±2mA/cm².

                                      TABLE 2                                      __________________________________________________________________________     SUMMARY OF EFFECT OF THE SOLUTION TEMPERATURE DURING                           POLYMERIZATION ON THE HALF-CELL BATTERY PERFORMANCE.sup.a                      OF THE POLYANILINE/TOSYLATE ELECTRODES                                         AT ±2 mA/cm.sup.2                                                                        PAN 86 PAN 83 PAN 81 PAN 85                                       __________________________________________________________________________     Electrode substrate                                                                         3D fat posts                                                                          3D fat posts                                                                          3D fat posts                                                                          3D fat posts                                 Starting materials                                                                          0.1 M aniline                                                                         0.1 M aniline                                                                         0.1 M aniline                                                                         0.1 M aniline                                             0.1 M H.sub.2 SO.sub.4                                                                1 M tosylate                                                                          1M tosylate                                                                           1 M tosylate                                 Solution pH  1.4    0.65   0.65   0.65                                         Solution temperature (°C.)                                                           20     20     30     40                                           Preparation method                                                                          PC.sup.b                                                                              PC.sup.b                                                                              PC.sup.b                                                                              PC.sup.b                                     Total coulombs                                                                              4 hr., 2.4 C                                                                          4 hr., 18.0 C                                                                         4 hr., 23.4 C                                                                         0.75 hr., 18 C                               Weight (mg)  0.6    18.3   24.3   11.8.sup.c                                   V.sub.oc (V) 0.46   0.43   0.45   0.39                                         I.sub.sc (mA/cm.sup.2)                                                                      0.04   0.02   0.13   0.07                                         Capacity (Ah/kg)                                                                            74.1   21.8   17.1   16.5                                         Coulomb eff. (%)                                                                            94     59     52     82                                           E.sub.out (Wh/kg)                                                                           35.8   10.8   8.3    8.4                                          __________________________________________________________________________      .sup.a Half-cell battery test was performed in 1 M ZnSO.sub.4 (pH 2.3) by      cycling potential between 0.35 V and 0.8 V vs. SCE at a constant               chargedischarge rate of ±2 mA/cm.sup.2.                                     .sup.b Potential cycled at 100 mV/sec between -0.2 V and +0.8 V vs. SCE.       .sup.c Film was flaky and loose, some material lost during rinsing after       polymerization.                                                          

The coulomb efficiency of the polyaniline/tosylate polymer electrodes improves dramatically as the charge-discharge current density increases, reaching almost 100 percent at ±10 to ±20 mA/cm² [see FIG. 7B]. Moreover, the charge capacity of the polyaniline/tosylate electrodes remain relatively unchanged with an increase of the current density, while the capacity of the conventional polyaniline electrode quickly degrades [see FIG. 7A]. This indicates that the polyaniline/tosylate electrodes are chemically more stable, presumably because the fixed anion (SO₃ -) sites allow H⁺ ions to be primarily mobile ions during the charge-discharge process, forming a useful cathode in an aqueous, high-current-density polymer battery.

ELECTROPOLYMERIZATION

The electrochemical polymerization method (potential-cycling method vs. constant voltage method) as well as the effect of pretreatment (cycling potential in 0.1 M H₂ SO₄ prior to the testing) is summarized in Table 4.

                                      TABLE 4                                      __________________________________________________________________________     SUMMARY OF EFFECT OF THE COMPOSITION                                           OF THE STARTING POLYMERIZATION SOLUTION                                        ON THE HALF-CELL BATTERY PERFORMANCE.sup.a                                     OF THE POLYANILINE/TOSYLATE ELECTRODE AT ±2 mA/cm.sup.2                                  PAN 96  PAN 93 PAN 92 PAN 95                                      __________________________________________________________________________     Electrode substrate                                                                         flat    flat   3D flat                                                                               flat                                        Starting materials                                                                          0.05 M aniline                                                                         0.1 M aniline                                                                         0.2 M aniline                                                                         0.2 M aniline                                            1 M tosylate                                                                           1 M tosylate                                                                          1 M tosylate                                                                          0.8 M tosylate                              Solution pH  0.65    0.65   0.65   1.1                                         Solution temperature (°C.)                                                           20      20     20     20                                          Preparation method                                                                          PC.sup.b                                                                               PC.sup.b                                                                              PC.sup.b                                                                              PC.sup.b                                    Total coulombs                                                                              12 hr, 6.1 C                                                                           4 hr, 3.7 C                                                                           6.5 hr, 7.0 C.                                                                        4 hr. 3.2 C                                 Weight (mg)  8.4     3.9    6.4    2.9                                         V.sub.oc (V) 0.43    0.43   0.03.sup.c                                                                            0.45                                        I.sub.sc (mA/cm.sup.2)                                                                      0.46    0.76   0.3    0.13                                        Capacity (Ah/kg)                                                                            17.9    24.9   25.1   26.8                                        Coulomb eff. (%)                                                                            87      86     93     90                                          E.sub.out (Wh/kg)                                                                           9.1     12.7   12.6   13.1                                        __________________________________________________________________________      .sup.a Half-cell battery test was performed in 1 M ZnSO.sub.4 (pH 2.3) by      cycling potential between 0.35 V and 0.8 V vs. SCE at a constant               chargedischarge rate of ±2 mA/cm.sup.2.                                     .sup.b Potential cycle at 100 mV/sec between -0.2 V and +0.8 V vs. SCE.        .sup.c The film partly peeled off.                                       

The polyaniline/tosylate prepared by applying a constant potential of 0.7 V vs SCE (PAN 103) exhibits fair performance (Table 5). When the potential is increased to 0.8 V, the resulting film is very powdery and peels off as soon as it is blown dry. When a constant potential of 0.65 V is used, the film takes a long time to grow, and the battery performance is not very good (PAN 104). The best results are obtained when the films grown by the potential-cycling method are pretreated by cycling between -0.2 V and 0.8 V at 100 mV/second in 0.2 M H₂ SO₄ for 2 hours (PAN 99). Pretreatment improves the half-cell battery performance by about 50 percent over the previous data (e.g. PAN 95); capacity and energy density became -40 Ah/kg and about 20 Wh/kg, respectively. This improvement is likely due to leaching out of the excess of tosylate ions, which are not incorporated into the polyaniline matrix reducing the effective weight of the electrode. No further improvement is observed when the pretreatment was continued for 12 hours (PAN 100).

                                      TABLE 5                                      __________________________________________________________________________     SUMMARY OF EFFECT OF ELECTROCHEMICAL POLYMERIZATION METHOD                     AND PRETREATMENT ON THE HALF-CELL BATTERY PERFORMANCE.sup.a                    OF THE POLYANILINE/TOSYLATE ELECTRODE AT ±2 mA/cm.sup.2                                  PAN 103 PAN 104 PAN 99 PAN 100                                    __________________________________________________________________________     Electrode substrate                                                                         flat    flat    flat   flat                                       Starting materials                                                                          0.2 M aniline                                                                          0.2 M aniline                                                                          0.1 M aniline                                                                         0.1 M aniline                                           0.8 M tosylate                                                                         0.8 M tosylate                                                                         1 M tosylate                                                                          1 M tosylate                               Solution pH  1.1     1.1     0.65   0.65                                       Solution temperature (°C.)                                                           20      20      20     20                                         Preparation method                                                                          0.7 V for 0.5 hr                                                                       0.65 V for 4 hr                                                                        PC.sup.b for 4 hr                                                                     PCV.sup.b for 4 hr                         Total coulombs (C)                                                                          4       4       4.1    4.1                                        Weight (mg)  2.7     3.5     4.7    4.5                                        Pretreatment --      --      2 hr.sup.c                                                                            12 hr.sup.c                                Capacity (Ah/kg)                                                                            29.1    17.1    38.4   40.3                                       Coulomb eff. (%)                                                                            93      96      96     87                                         E.sub.out (Wh/kg)                                                                           14.8    8.2     19.4   19.7                                       __________________________________________________________________________      .sup.a Half-cell battery test was performed in 1 M ZnSO.sub.4 (pH 2.3) by      cycling potential between 0.35 V and 0.8 V vs. SCE at a constant               chargedischarge rate of ±2 mA/cm.sup. 2.                                    .sup.b Potential cycle at 100 mV/sec between -0.2 V and +0.8 V vs. SCE.        .sup.c Cycled in 0.1 M H.sub.2 SO.sub.4.                                 

The most striking feature of the polyaniline/tosylate polymer films is that, in addition to being highly conductive, they exhibit a second conductive region (permanently conductive), which extends to a higher potential region, up to 1.5 V. This also means that the polyaniline/ tosylate films are chemically more stable than conventionally made polyanilines. The unique resistance vs. voltage characteristics of the polyaniline/tosylate is also used to design new molecular electronic devices such as an organic transistor and memory device.

In another preferred embodiment, the polymer is produced under the following conditions wherein the aniline is at a starting concentration of about 0.1M, the p-toluensesulfonic acid is at a starting concentration of about 1M, the potential range is between about -0.1 and +0.9 V versus SCE, the scan rate is about 0.1V per second, the total coulomb is about 1.1, and the time is about 15 minutes.

In a preferred embodiment the polymer is prepared wherein the aniline is at a starting concentration of about 0.1M, the p-tolunesulfonic acid is at a concentration of about 1M, the potential range is between about -0.2 and +0.8 V versus SCE, the scan rate is about 0.1 V per second, and the total coulombs is 6.0 and the time is about 6.5 hours.

In another preferred embodiment, the self-doped polyaniline is produced having about a 0.1M starting concentration of aniline and about 1M p-toluenesulfonic acid, a potential range of between about -0.2 and +0.8 volts versus SCE and a scan rate of about 0.1 volt per second. The produced polymer is a function of time and the size of the electrode. In a more preferred embodiment of the above reaction conditions, the time is 3 hr. and the total coulomb is 6.1.

In a more preferred embodiment, the self-doped polyanine is produced having about a 0.1M starting concentration of aniline and 1M starting concentration of aniline and 1M benzenesulfonic acid, a potential range of between about -0.1 to +0.9 volts versus SCE, and a scan rate of about 0.1 volts per second. The thickness of the produced polymer is a function of time and size of the electrode. In a more preferred embodiment of the above reaction conditions, the time is hr. and the total coulomb is 5.5.

In a preferred embodiment the self-doped polyaniline is produced having a starting aniline concentration of 0.1M, a 12.5 percent by volume starting polyvinylsulfonic acid concentration, a potential range of between about -0.2 to +0.8 V (versus SCE) and a scan rate of about 0.1 V per second. The thickness of the polymer is a function of the time of reaction and size of the electrode. In a more preferred embodiment of the above conditions, the time is for about 16 hr. and a total coulomb is 5.4.

In a preferred embodiment, the self-doped polyaniline is produced having about a 0.1M starting concentration of aniline, a 1M starting concentration of trifluoromethanesulfonic acid, a potential range of about -0.1 to +0.9 versus SCE and a scan rate of 0.1 V per second. The thickness of the polymer is a function of the time and the size of the electrode. In a more preferred embodiment of the above conditions, the time is about 2.5 hr. and the total coulomb is about 6.1.

The NAFION®-Polyaniline/Tosylate Composite Electrodes

A major problem to be overcome in the development of an aqueous, large-current polymer battery is the loss of the stored charge through a self-discharging process. As summarized in Table 6, self-discharging (i.e. the coulomb efficiency decreases as the rest time increases) was observed for both a conventional polyaniline polymer electrode made in H₂ SO₄ (PAN 86) and a polyaniline/tosylate polymer electrode [PAN 73).

                                      TABLE 6                                      __________________________________________________________________________     COULOMB EFFICIENCY OF THREE ELECTRODE MATERIALS                                AS A FUNCTION OF REST TIME.sup.a                                               (Percent)                                                                               Polyaniline/H.sub.2 SO.sub.4                                                   (conventional)                                                                           Polyaniline/Tosylate                                                                           Nafion/Polyaniline/Tosylate                          PAN 86.sup.b                                                                        Pan 86                                                                              PAN 73.sup.c                                                                        PAN 73                                                                              PAN 108.sup.d                                                                        PAN 105                                                                             PAN 106                                                                             PAN 107                           __________________________________________________________________________     Electrolyte (1M)                                                                        Tosylate                                                                            ZnSO.sub.4                                                                          Tosylate                                                                            ZnSO.sub.4 ZnSO.sub.4                                  Rest Time(s)                                                                     0      93   99   84   79   89    90   97   99                                 10      93   98   --   --   87    94   99   97                                 100     86   87   83   80   79    84   89   86                                1000     63   65   64   68   49    59   72   67                                __________________________________________________________________________      .sup.a The electrode was first charged with +2 mA/cm.sup.2 until the           electrode potential reached 0.8 V; the electrode was kept unbiased for a       certain time as indicated as the rest time. Then, the electrode was            discharged with -2 mA/cm.sup.2 until the potential became 0.35 V.              .sup.b Conventional polyaniline electrode.                                     .sup.c Standard polyaniline/tosylate electrode: 0.1 M aniline/1 M tosylat      by the potentialcycling method.                                                .sup.d Starting solution: 0.2 M aniline/0.8 M tosylate (pH adjusted to 0.      by H.sub.2 SO.sub.4), prepared by the potentialcycling method.           

RESISTANCE MEASUREMENTS USING AN INTERDIGITATED MICROELECTRODE ARRAY

Using the interdigitated microelectrode array (gold or platinum) approach, the resistance of polyaniline films is measured that have different ratios of aniline to tosylate in the polymerization solution as a function of applied potential. The results are presented in FIG. 2 together with data obtained with the conventional polyanilines. Some minor difference in the magnitude of resistance is observed between the platinum electrode and the gold electrode, which is presumably due to the difference in the surface electrochemical properties of gold and platinum (e.g. surface oxide). The composition of 0.7 M tosylate and 0.3 M aniline failed to produce a stable film (PAN R3). The following is a summary:

The polyaniline/tosylate films are much more conductive (estimated conductivity is on the order of about 1 to 100 S/cm) than any previously made polyaniline films in the potential window for the conductive region of polyaniline (i.e. 0.1 to 0.6 V vs. SCE).

There is a permanently doped region in the potential range 0.8 to about 1.5 V in the polyaniline/tosylate films, while the conventional polyanilines show a transition from conductor to insulator at about 0.7 V and start to deteriorate upon application of a voltage greater than about 0.7 V.

The conductivity of the polyaniline/tosylate films increases with an increase of the ratio to tosylate to aniline in the polymerization solution.

In an attempt to reduce the self-discharge problem, the composite system NAFION ®/polyaniline/tosylate is studied as a cathode battery electrode. Electrodes made by two methods are evaluated.

Method 1--Polyaniline/tosylate is polymerized on a NAFION® film-coated electrode.

Method 2--A multilayer Nafion film is deposited on the polyaniline/tosylate electrode.

Several polyaniline/tosylate films are grown on a Nafion-coated electrode by the potential-cycling method (PAN 105) and by the constant-potential method (+0.65 and +0.7 V vs. SCE: PAN 106 and PAN 107). Also one electrode is prepared from a solution containing 0.2 M aniline and 0.8 M tosylate; its pH is adjusted to 0.7 (the same pH as the mixture of 0.1 M aniline and 1 M tosylate) by adding H₂ SO₄ (PAN 108).

The results of coulomb efficiency vs. rest-time experiments presented in the righthand side of Table 6 indicate that Method 1 does not reduce the self-discharge problem. The resistance vs. voltage plots are presented in FIG. 8; the curves were almost identical for the polyaniline/tosylate polymer films with or without NAFION®. The polyaniline/tosylate polymer film made from 0.2 M aniline and 0.8 M tosylate by the potential-cycling method became more conductive after being cycled in H₂ SO₄ for 5.5 hours. The half-cell battery test results are summarized in Table 7. Smaller values of charge capacity and energy density were obtained when the polyaniline/tosylate was prepared in a Nafion film, because Nafion increases the electrode weight.

                                      TABLE 7                                      __________________________________________________________________________     SUMMARY OF THE HALF-CELL BATTERY PERFORMANCE.sup.a OF THE                      NAFION/POLYANILINE/TOSYLATE ELECTRODES AT ±2 mA/cm.sup.2                                 PAN 105 PAN 106 PAN 107 PAN 108                                   __________________________________________________________________________     Electrode substrate                                                                         Nafion-coated                                                                          Nafion-coated                                                                          Nafion-coated                                                                          Nafion-coated                                          flat    flat    flat    flat                                      Starting materials                                                                          0.2 M aniline                                                                          0.2 M aniline                                                                          0.2 M aniline                                                                          0.2 M aniline                                          0.8 M tosylate                                                                         0.8 M tosylate                                                                         0.8 M tosylate                                                                         0.8 M tosylate                            Solution pH  1.1     1.1     1.1     0.7.sup.b                                 Solution temperature (°C.)                                                           20      20      20      20                                        Preparation method                                                                          Pc.sup.c for 3 hr                                                                      0.65 V for 4 hr                                                                        0.7 for 0.5 hr                                                                         PC.sup.c for 3.5 hr                       Total coulombs (C)                                                                          4       4       4       7                                         Weight (mg)  4.2     3.7     4.7     8.7                                       Capacity (Ah/kg)                                                                            18.2    13.2    7.4     13.3                                      Coulomb eff. (%)                                                                            90      96      99      90                                        E.sub.out (Wh/kg)                                                                           7.1     5.9     3.3     6.4                                       __________________________________________________________________________      .sup.a Half-cell battery test was performed in 1 M ZnSo.sub.4 (pH 2.3) by      cycling potential between 0.35 V and 0.8 V vs. SCE at a constant               chargedischarge rate of ±2 mA/cm.sup.2.                                     .sup.b Adjusted by H.sub.2 SO.sub.4.                                            .sup.c Potential cycle at 100 mV/sec between -0.2 V and +0.8 V vs. SCE. 

The best results in reducing the loss of battery capacity through self-discharging are obtained when a few layers of NAFION® film were case on the already prepared polyaniline/tosylate polymer electrode. Successive Nafion films are deposited; each layer consisted of 50μL/cm² of the 5:1 diluted pre-ion-exchanged Nafion solution Table 7 summarizes the results. After the application of a single layer of NAFION®, the loss of charge capacity through self-discharging is dramatically reduced for both the conventional polyaniline electrode and the polyaniline/tosylate electrode. Further addition of NAFION® layers results in only slight improvement.

The following Examples are meant to be illustrative and descriptive only. They are not to be construed as being limiting in any way.

The chemicals and reagents are available in high purity reagent grade from chemical supply houses such as Aldrich Chemical of Milwaukee, Wisconsin, Kodak, Rochester, N.Y. or those identified in Chemical Sources, U.S.A., published annually by Directories Publishing, Inc., of Boca Ratan, Fla. NAFION® is also available from Solution Technology, Inc. of Philadelphia, Pa.

EXAMPLE 1 ELECTROPOLYMERIZATION OF COMPOSITION RATIOS OF ANILINE/TOSYLATE

(A) 1 M Tosylate/0.5 M aniline--1 M tosylate solution is prepared The solution is warmed to 30° C. by placing the beaker in a water bath and 0.5 M aniline is added. Initially, the solution remains clear after a gentle agitation; however, gradually white precipitate starts to form by a direct chemical reaction between aniline and tosylate and eventually forms a hard lump.

(B) 0.5 Tosylate/0.5 M aniline--The solution is prepared as above in step 1(A) (the pH of the 0.5 M tosylate solution is 1.56); however, the solution stays clear in 30° C. water bath. The electrochemical polymerization is attempted on a 3D fat posts electrode (PAN 90 and 91). Initially, the polymerization reaction occurs normally; however, after about 10 to 15 minutes, the existing grown film starts to slow the polymerization process--the film appears to be very insulating--and finally, no further film growth is observed.

(C) M Tosylate/1.5 M aniline--The starting solution is clear but dark yellow. Polymerization (PAN 97) occurs initially, but the film becomes insulating as indicated by CV growth curve. Not much of the film is left after the experiment is terminated; the remaining film looks very loose and flaky and is washed away by rinsing with water.

(D) 1 M Tosylate/0.3 M aniline, 0.8 tosylate/0.3 M aniline--As observed with the 1 M tosylate/0.5 M aniline case, precipitation occurs immediately and a lump forms.

Usable polymer films of polyaniline/tosylate are formed when the concentration range is limited to between about 0.8 and 1 M for tosylate and between about 0.05 and 0.2 M for aniline. The results of the half-cell battery test are summarized above in Table 4. No substantial difference in terms of the half-cell performance was observed when the concentration of aniline is increased from between about 0.1 M and 0.2 M or the concentration of tosylate is decreased from between about M to 0.8 M. However, a low concentration of aniline, i.e. 0.05 M, gives a poorer performance (PAN 96). A preferred concentration range is: aniline: 0.1 M to 0.2 M; tosylate: 0.8 M to 1 M.

EXAMPLE 2 BENZENESULFONIC-ACID-BASED SELF-DOPED POLYANILINE

A number of benzenesulfonate-doped polyanilines (PAN/Bs) are electrochemically synthesized either on a platinum-sputtered plain ceramic electrode or a platinum-covered three-dimensional "fat post" electrode in an aqueous solution containing 0.1 M aniline and 1 M benzenesulfonic acid (Bs), which produces pH of 1.5.

Tables 8 and 9 below summarize the synthesis conditions in detail. A potential-cycling method is used for most of the synthesis attempts because the other electrochemical approaches (i.e., constant-potential method and constant-current method) does not yield any workable polymers. For example, when a constant potential of 0.8 V with respect to a saturated calomel electrode (vs. SCE) is applied, the resulting polymer film (PAN3016) is extremely loose and flaky. The "best" surface morphology is obtained when benzenesulfonic-acid-doped polyaniline is prepared by a potential-cycling method at a scan rate of 0.1 V/s cycled between -0.1 V to +0.9 V vs. SCE. No polymer growth is observed when the potential is cycled between -0.2 V to +0.8 V vs. SCE, which is the standard electrochemical window for the conventional polyaniline made from 0.1 M aniline and 0.1 M sulfuric acid.

FIG. 9A shows a typical cyclic voltammogram during the polymerization of the PAN/Bs. The polymerization process is fast (e.g., the current on the order of 50 mA/cm² is involved after only 90 cycles of the polymerization), indicating that the PAN/Bs film is very conductive. As observed with the polyaniline/tosylate (PAN/Ts), an additional redox peak is seen about 0.2 V, which results from the oxidation of polyaniline by the incorporation of benzenesulfonic acid, i.e., SO₃ -group. The presence of the sulfonic groups within the polyaniline/benzenesulfonate is confirmed by an EDAX analysis, which showed the presence of a large amount of elemental sulfur. FIG. 9B illustrates a typical cyclic voltammogram of grown PAN/Bs film in 0.5 M Na₂ SO₄ aqueous solution, which shows a mostly featureless curve mostly consisting of a large double-layer charge-discharge current.

FIG. 10 shows a typical surface morphology of the self-doped PAN/Bs at 40 and 200 micrometer scale prepared by the potential cycling method The surface exhibits a very rough, powdery thick film with many cracks. The grown films are very loose and flaky, which makes it difficult to conduct further characterization study of the films. It is impossible to dry the films in a desiccator because the polymer turns into powder when the surface is completely dried. Several attempts were made to improve the quality of the PAN/Bs films prepared by potential cycling method (see Table 9). In particular, several slower potential scan rates (i.e. 20, 50 and 75 mV/s) and a higher aniline-to-Bs ratio (i.e., 0.2 M aniline and 1 M Bs) were attempted. Not one of the polymer films produced better morphology than those prepared form 0.1 M aniline and 1 M Bs at a scan rate of 100 mV/s.

FIG. 11 presents the resistance measurements using the interdigitated microelectrode array method developed. The shape of the resistance versus potential plot is similar to that observed with PAN/Ts in that, besides being more conductive than the conventional PAN films, there is a permanently conductive region in the potential range of 0.8 to 1.5 V.

The battery performance characteristics of some of the PAN/Bs electrodes are evaluated after a thin layer of Nafion solution (50 μL of 5:1 diluted Nafion solution which produces an approximately 1-μm thick Nafion film after dried) is deposited onto the surface of each electrode immediately following polymerization. FIG. 12 shows the coulomb efficiency and capacity of electrode PAN3016 as a function of charge-discharge current density. The half-cell battery performance is evaluated in 1 M ZnSO4 (pH 2.3) by cycling potential between 0.35 V and 0.8 V vs. SCE at a constant charge-discharge rate using a platinum counter electrode. The complete battery performance using a zinc sheet as anode is measured by cycling cell voltage between 1.7 and 1.35 vs. SCE.

                  TABLE 8                                                          ______________________________________                                         ELECTROCHEMICAL SYNTHESIS CONDITIONS                                           FOR BENZENESULFONIC-ACID-BASED                                                 SELF-DOPED POLYANILINES                                                        Unless otherwise noted, all electrodes                                         planar platinum on ceramic substrate.                                          Elec-                   Total      Mor-                                        trode Preparation Method                                                                               Coulomb    phology                                     ______________________________________                                         PAN   0.1 M aniline/1 MBs*:                                                                            0.7 h, 8.3 C                                                                              Flaky                                       3003  Potential cycling,                                                             0 ⃡ +1 V.sup. , 75 mV/s                                      PAN   0.1 M aniline/1 MBs*:                                                                            0.3 h, 5.4 C                                                                              Flaky                                       3004  Potential cycling,                                                             0 ⃡ +1 V, 50 mV/s                                            PAN   0.1 M aniline/1 M Bs*:                                                                           0.7 h, 6.8 C                                                                              Flaky                                       3005  Potential cycling,                                                             0 ⃡ 1 V.sup. , 50 mV/s                                       PAN   0.1 M aniline/1 M Bs*:                                                                           0.8 h, 4.2 C                                                                              Flaky                                       3006  Potential cycling,                                                             0 ⃡ 1 V.sup. , 20 mV/s                                       PAN   0.1 M aniline/1 M Bs*:                                                                           0.9 h, 4.0 C                                                                              Flaky                                       3007  Potential cycling,                                                             0 ⃡ 1 V.sup. , 20 mV/s                                       PAN   0.2 M aniline/1 M Bx:                                                                            1.7 h, 3.0 C                                                                              Flaky                                       3008  Potential cycling,                                                             -0.2 ⃡ +0.8 V.sup. , 100 mV/s                                PAN   0.2 M aniline/1 M Bs* with                                                                       1.3 h, 0.13 C                                                                             Flaky                                       3009  Nafion:                                                                        Potential cycling,                                                             -0.2 ⃡ +0.8 V.sup. , 100 mV/s                                ______________________________________                                          *Bs: Benzenesulfonic acid                                                      .sup. All the potential values reported are with respect to SCE (saturate      calomel electrode).                                                      

                                      TABLE 9                                      __________________________________________________________________________     ELECTROCHEMICAL SYNTHESIS CONDITIONS AND BATTERY PER-                          FORMANCE OF BENZENESULFONIC-ACID-BASED                                         SELF-DOPED POLYANILINES                                                        Unless otherwise noted, all electrodes                                         planar platinum on ceramic substrate                                                                           Coulomb                                                             Total  Weight                                                                             Efficiency                                                                           Capacity                                 Electrode                                                                             Preparation Method                                                                           Coulomb                                                                               (mg)                                                                               (%)   (Ah/kg)                                  __________________________________________________________________________     PAN 3010                                                                              0.1 M aniline/1 M Bs*:                                                                         4 h, 0.6 C                                                     Constant current,                                                              0.1 mA/cm.sup.2                                                         PAN 3011                                                                              0.1 M aniline/1 M Bs*:                                                                       0.2 h, 5.0 C                                                     Constant potential,                                                            +0.8 V                                                                  PAN 3012                                                                              0.1 M aniline/1 M Bs*:                                                                       0.5 h, 7.35 C                                                    Constant potential,                                                            +0.7 V                                                                  PAN 3013.sup.                                                                         0.1 M aniline/1 M Bs*:                                                                       1.5 h, 6.2 C                                                                          19.4                                                                               100   3.92                                            Potential cycling,                                                             -0.1 ⃡ +0.9 V, 100 mV/s                                     PAN 3014.sup.                                                                         0.1 M aniline/1 M Bs*:                                                                       2.5 h, 2.7 C                                                                          2.5                                                       Potential cycling,                                                             -0.1 ⃡ +0.9 V, 100 mV/s                                     PAN 3015.sup.                                                                         0.1 M aniline/1 M Bs*:                                                                       1.5 h, 9.8 C                                                                          21.1                                                                               100   4.47                                            Potential cycling,                                                             -0.1 ⃡ + 0.9 V, 100 mV/s                                    PAN 3016.sup.                                                                         0.1 M aniline/1 M Bs*:                                                                         1 h, 28.8 C                                                                         72.5                                                                                99   2.66                                            Constant potential,                                                            +0.8 V                                                                  __________________________________________________________________________      *Bs: Benzenesulfonic acid                                                      .sup. 30 μl of 3:1 MEW NAFION solution deposited immediately after          polymerization                                                                 .sup. Working electrode with platinum black                                    .sup. "Old Coco" platinum electrode                                      

EXAMPLE 3 POLYVINYLSULFONIC-ACID-BASED-SELF-DOPED POLYANILINE 1. Preparation of Polyvinylsulfonic Acid

The starting polymer used is polyvinylsulfonate sodium salt (Polyscience Inc., 25% in water, MW 2000). Polyvinylsulfonic acid is prepared by washing commercially available polyvinylsulfonate sodium salt in an ion-exchange column. The exchange column used is Amberlite IR-120 plus ion exchange resin (Polyscience, Inc.) The ion exchange procedure is as follows:

(1) The ion exchange resins are packed and washed with 6 M HCl solution, followed by rinsing with deionized water before use. This preconditioning process ensures that the ion exchange resins are the desired ionic formula.

(2) 25mL of polyvinylsulfonate sodium salt solution (pH 9.5) is passed through the exchange column at a slow flow rate (approximately 15 mL/hour). The pH of the filtrate, i.e. polyvinyl-sulfonic acid, should be about 1.5.

(3) Rinse the ion exchange resins with deionized water until all the polyvinylsulfonates have pass through the exchange column, i.e., until the pH of the filtrate becomes neutral.

(4) The exchanged column is rejuvenated by washing with 30 mL of 6 M HCl solution at same slow flow rate. The excess HCl is then rinsed off with deionized water.

(5) The polyvinylsulfonic acid produced in Step (2) is passed through the exchange column one more time to ensure the complete ion exchange process [repeat Step (2) above].

(6) Double the volume of the prepared polyvinylsulfonic acid by adding deionized water so that the actual concentration of the acid becomes onehalf of the concentration of the stock solution (i.e., 12.5% in water).

2. Polymerization and Results

The polyaniline/polyvinylsulfonates (PAN/PVSA) are prepared electrochemically in an aqueous solution containing 0.1 M aniline and 12.5% polyvinylsulfonic acid (pH=1.5) either on the planar platinum sputtered ceramic electrode or on the three-dimensional fat post electrode. Several electrodes are made by different electrochemical polymerization methods (see Table 10) and characterized for the battery application. The polymer films prepared by the potential cycling method with a standard electrochemical window of -0.2 V to +0.8 V vs. SCE exhibits the most uniform surface structure.

                  TABLE 10                                                         ______________________________________                                         ELECTROCHEMICAL SYNTHESIS CONDITIONS                                           FOR POLYVINYLSULFONIC-ACID                                                     SELF-DOPED POLYANILINES                                                        Elec-                   Total      Weight                                      trode Preparation Method                                                                               Coulomb    (mg)                                        ______________________________________                                         PAN   0.1 M aniline/12.5%                                                                                2 h, 2.2 C                                           3017* PVSA.sup. :                                                                    Potential cycling,                                                             -0.2 ⃡ +0.8 V, 100 mV/s                                      PAN   0.1 M aniline/12.5%                                                                                1 h, 3.6 C                                                                              2.7                                         3018.sup.                                                                            PVSA.sup. :                                                                    Potential cycling,                                                             -0.2 ⃡ +0.8 V,100 mV/s                                       PAN   0.1 M aniline/12.5%                                                                                1 h, 3.6 C                                                                              0.9                                         3019.sup.                                                                            PVSA.sup. :                                                                    Constant current,                                                              1 mA/cm.sup.2                                                            PAN   0.1 M aniline/12.5%                                                                              0.3 h, 6.3 C                                                                              1.2                                         3020.sup.                                                                            PVSA.sup. :                                                                    Constant potential,                                                            +0.8 V                                                                   PAN   0.1 M aniline/12.5%                                                                               64 h, 7.6 C                                                                              3.3                                         3021.sup.                                                                            PVSA.sup. :                                                                    Potential cycling,                                                             -0.2 ⃡ +0.8 v, 100 mV/s                                      ______________________________________                                          *Planar sputtered ceramic electrode                                            .sup. PVSA: Polyvinylsulfonic acid                                             .sup. Three-dimensional "fat post" electrode                             

FIGS. 13A and 13B show a typical cyclic voltammogram of the PAN/PVSA during the polymerization, and a cyclic voltammogram of the grown film in 0.5 M Na₂ SO₄ solution. These CV curves shown the characteristic features of the self-doped polyaniline observed with the PAN/Ts and PAN/Bs. The presence of the sulfonic group (--SO₃ -) is confirmed by the large sulfur peak observed in an EDAX analysis. Unlike the PAN/Bs film, the PAN/PVSA exhibits a surface morphology at 200 and 40 micrometer scale. (See FIG. 14) which is similar to that of PAN/Ts, i.e. an ultrafine microstructure with a highly electroactive surface, which makes the film attractive for the battery application.

The results of the resistance measurements of the PAN/PVSA using the interdigitated microelectrode array method are presented in FIG. 15. The PAN/PVSA films are more conductive that the conventional PAN/H₂ SO₄ ; however, they are more resistive than the other self-doped polyaniline films (PAN/Ts and PAN/Bs). FIGS. 16A and 16B illustrate the coulomb efficiency and capacity of various PAN/PVSA electrodes as a function of charge/discharge current density for both half-cell battery and complete batter (zinc as anode). Generally speaking, the battery performance of the PAN/PVSA electrodes are comparable is comparable to that of the PAN/tosylate electrodes.

EXAMPLE 4 Trifluoromethanesulfonic-Acid-Based Self-Doped Polyaniline

The polyaniline/trifluoromethanesulfonates are electrochemically polymerized in an aqueous solution containing M trifluoromethanesulfonic acid (TFMSA) and 0.1 M aniline either on the planar platinum sputtered ceramic electrode or on the three-dimensional fat post electrode. The 1 MTFMSA solution (PH=1.15) is prepared form 98% stock solution (Chemical Dynamics Corporation). Several PAN/TFMSA electrodes are mostly prepared by the potential cycling method (see Table 11), because the potential cycling method produces the best polymer films. However, when the conventional electrochemical window for potential cycling (-0.2 to +0.8 V vs. SCE) is applied, the growth of films is extremely slow; therefore, the window is shifted to -0.1 to +0.9 V.

A sharp, well-defined redox peak is seen around 0.2 V vs. SCE in the cyclic voltammogram during the polymerization (FIG. 17A), indicating a smooth incorporation of sulfonic groups (--SO₃) into the film (the presence of a large sulfur peak is shown in an EDAX analysis). This observation is probably related to the fact that trifluoromethanesulfonic acid has a relatively low molecular weight of 150.07. The cyclic voltammogram of a grown film of PAN/TFMSA is 0.5 M Na₂ SO₄ solution [FIG. 17B] is similar to that observed with PAN/Ts. Unfortunately, the morphology of the PAN/TFMSA (FIG. 18) exhibits a thick film with many cracks that is rough and brittle, although it is slightly more smooth than the PAN/Bs films.

The results of the resistance measurements of PAN/TFMSA electrodes made using the interdigitated microelectrode. array method are shown in FIG. 19. The residual electrical properties are seen in FIG. 19 in the region of about 0.8 to 1.4 volts. The PAN/TFMSA films are more conductive than the conventional PAN/H₂ SO₄ films, and the resistance vs. potential curves of PAN/TFMSA are almost identical to those obtained with PAN/Ts. FIG. 20 illustrates the coulomb efficiency and capacity of various PAN/TFMSA electrodes as a function of charge-discharge current density. The performance of these electrodes are comparable to that of the PAN/tosylate electrodes.

                  TABLE 11                                                         ______________________________________                                         ELECTROCHEMICAL SYNTHESIS CONDITIONS                                           FOR TRIFLUOROMETHANESULFONIC-ACID                                              SELF-DOPED POLYANILINES                                                        Elec-                   Total      Weight                                      trode Preparation Method                                                                               Coulomb    (mg)                                        ______________________________________                                         PAN   0.1 M aniline/1 M 18.5 h, 6.6 C                                                                             1.9                                         3022* TFMSA.sup. :                                                                   Potential cycling,                                                             -0.2 ⃡ +0.8 V, 100 mV/s                                      PAN   0.1 M aniline/1 M  2.6 h, 5.1 C                                                                             2.9                                         3023* TFMSA.sup. :                                                                   Potential cycling,                                                             -0.1 ⃡ +0.9 V, 100 mV/s                                      PAN   0.1 M aniline/1 M  12 h, 14.6 C                                                                             20.9                                        3024.sup.                                                                            TFMSA.sup. :                                                                   Potential cycling,                                                             -0.1 ⃡ +0.9 V, 100 mV/s                                      PAN   0.1 M aniline/1 M  9.5 h, 7.0 C                                                                             8.1                                         3025.sup.                                                                            TFMSA.sup. :                                                                   Constant current,                                                              0.2 mA/cm.sup.2                                                          PAN   0.2 M aniline/1 M  1.5 h, 10.3 C                                                                            16.2                                        3026* TFMSA.sup. :                                                                   Potential cycling,                                                             -0.1 ⃡ +0.9 V, 100 mV/s                                      PAN   0.2 M aniline/1 M  25 h, 35.5 C                                                                             6.7                                         3027.sup.                                                                            TFMSA.sup. :                                                                   Potential cycling,                                                             -0.3 ⃡ +0.8 V, 100 mV/s                                      ______________________________________                                          *Planar platinum sputtered ceramic electrode                                   .sup. TFMSA: Trifluoromethanesulfonic acid                                     .sup. Three-dimensional "fat post " electrode                            

ACCELERATED STABILITY TESTS

Accelerated stability tests are conducted using a cyclic voltammetry technique for four polyaniline electrodes to identify the most chemically stable polyaniline-dopant electrode within a typical electrochemical window for the charge-discharge conditions:

Polyaniline/benzenesulfonic acid/NAFION® [PAN/Bs/Nf]

Polyaniline/polyvinylsulfonic acid [PAN/PVSA]

Polyaniline/toluenesulfonic acid (tosylate) [PAN/Ts]

Polyaniline/trifluoromethanesulfonic acid [PAN/TFMSA]

In the case of polyaniline/benzenesulfonic acid, it is necessary to cover the polymer electrode with a NAFION® film because the grown film is very loose and flaky.

FIG. 21 shows the results. The potential is cycled between +0.35 V to +0.8 V (vs. SCE) in 12 M ZnSO₄ solution (pH 2.3); the scan rate is 20 mV/s and the cyclic voltammograms for cycles 100 and 100 are shown. There is hardly any change in shape of the two cyclic voltammogram curves for the PAN/Ts electrode and the PAN/TFMSA electrode, indicating that these electrodes are intrinsically stable. On the other hand, the PAN/Bs and the PAN/PVSA show considerable degradation after 100 cycles, which result in a substantial distortion in the cyclic voltammogram curves.

For a quantitative comparison, the current densities are calculated at +0.8V of cycle 10(I₁₀) and cycle 100 (I₁₀₀). A normalized parameter, I/I₁₀, where I =I₁₀ -I₁₀₀, is used to measure the stability of each electrode (see Table 12). Using this calculation, the stability decreases in the following sequence:

    PAN/TFMSA>PAN/Ts>>PAN/Bs(w/Nf)>PAN/PVSA

FIG. 22 is a plot of cell voltage as a function of time for accelerated charge/discharge cycles (60s/cycle) at +or -15 mA/cm² for the two most chemically stable self-doped polyaniline electrodes: PAN/TFMSA (FIG. 22A) and PAN/Ts (FIG. 22B). Both electrodes are preparaed on the "fat-posts" three-dimensional electrode. The PAN/TFMSA shown no sign of degradation after about 600 cycles, while the PAN/Ts shown a slight degradation after about 500 cycles. This observation is consistent with the stability sequence listed above.

SELF-DISCHARGE TEST

In general, fast self-discharge is a serious problem in many polymeric electrodes. To identify the best self-doped polyaniline electrode, a self-discharge test is performed on the four polyaniline electrodes listed earlier. The open-circuit voltgage (V_(oc)) is recorded of the cell (battery) comprising a self-doped polyaniline and a zince sheet as anode as a function of time at constant temperature (25° C.) in 1 M ZnSO₄ solution (pH 2.3) for up to about 20 hours. This method is time-consuming, but otherwise convenient because the results are insensitive to the coulombic capacity of the electrode, the quality of electric contacts in the system, and the conductivity of the electrolyte layer.

FIG. 23 shows V_(oc) as a function of time for the four different polyaniline electrodes. This solution was kept purged with N₂ gas to avoid the influence of O₂. Each electrode is synthesized using approximately the same amount of coulombs (approximately 6C). The surface morphology of the electrodes is shown in FIGS. 24 and 25. It is interesting to observe that the two most chemically stable electrodes identified in the previous experiment-PAN/Ts and PAN/TFMSA-also show a very stable open-circuit voltage after an initial slight drop of the voltage. In addition, these two electrodes exhibit a highly microporous morphology (although the PAN/TFMSA shows some minor macrocracks), while other two electrodes (PAN/PVSA) and PAN/Bs) exhibit a compact, smooth surface. For a quantitative comparison, we have calculated the decrease in V_(oc) at 60000 s (16.7 hours) for each electrode. Using this calcuation, the self-discharge rate increases in the sequence:

    PAN/Ts˜PAN/TFMSA>>PAN/PVSA>>PAN/Bs(w/Nf).

Table 12 summarizes the surface morphology, conductivity, basic battery performance, self-discharge rate, and stability (cyclability) of the four self-doped polyanilines made with different organic sulfonic acid dopants. Based on the results presented in Table 2 (in particular, the results of the accelerated stability test and the self-discharge test), polyaniline/trifluoromethanesulfonic acid [PAN/TFMSA] and polyaniline/toluenesulfonic acid (tosylate) [PAN/TS] are useful self-doped polyanilines for deveopment of a polymer battery, e.g. with a zinc anode.

All self-doped polyanilines exhibit a higher conductivity than the conventional PAN/H₂ SO₄ films and also exhibit a permanently conductive region at potentials above 0.7 to 0.8 V vs. SCE. However, the surface morphology of the four self-doped polyanilines are quite different, and the PAN/Ts exhibits the best morphology. The PAN/TFMSA exhibits the best coulomb efficiency and may exhibit a high battery capacity after the polymerization conditions are optimized.

The observed almost featureless CV curves in aqueous solution with all of the four self-doped polyanilines strikingly resemble a typical CV curve for the conventional polyaniline electrode (e.g., made from 1 M aniline in aqueous 2 M HClO₄) measured in a nonaqueous solution (e.g., 1 M LiClO₄)/propylene carbonate). This resemblance supports the intrinsic superior stability of the self-doped polyanilines in aqueous solutions over the conventional polyanilines because the conventional polyanilines are known to be unstable in aqueous solutions but reasonably stable in nonaqueous solutions. Therefore, the development of an aqueous polymer battery based on the self-doped polyaniline is achieved.

                                      TABLE 12                                     __________________________________________________________________________     BATTERY PERFORMANCE OF SELF-DOPED POLYANILINES                                                    PAN/                                                                           Trifluoro-                                                                            PAN/  PAN/                                                        PAN/  methane-                                                                              Polyvinyl-                                                                           Benzene-                                                    Toysylate                                                                            sulfonate                                                                             sulfonate                                                                            sulfonate                                      Characteristic                                                                              (Ts)  (TFSMA)                                                                               (PVSA)                                                                               (Bs)                                           __________________________________________________________________________     Morphology   Dense,                                                                               Slightly                                                                              Smooth,                                                                              Loose,                                                      smooth                                                                               powdery                                                                               uniform                                                                              flaky,                                                      durable            powdery                                        Resistance (Ω)                                                           High*        60    ≈100                                                                          600   100                                            Low.sup.     ≈1                                                                           2      30    ≈1                                     Capacity.sup.  (Ah/kg)                                                                      36    22     21    5                                              Coulomb efficiency.sup.  (%)                                                                86    92     92    92                                             Stability    Excellent                                                                            Excellent                                                                             Poor  Poor                                           V (volts)    1.39  1.38   1.36  1.33                                           ΔV.sup.  (volts)                                                                      0.09  0.09   0.26  0.47                                           ΔV/V (%)                                                                              6.4   6.5    19.0  34.9                                           I (mA/cm.sup.2)                                                                             16.3  16.8   12.6  1.5                                            ΔI (mA/cm.sup.2)                                                                      1.0   0.4    6.8   0.65                                           ΔI/I** (%)                                                                            6.1   2.4    54.0  43.3                                           __________________________________________________________________________      *Potential >0.7 V vs. SCE                                                      .sup. Potential 0 to 0.5 V vs. SCE                                             .sup. At ±2 mA/cm.sup.2                                                     .sup. V is opencircuit cell voltage of a battery (zinc sheet as anode;         ΔV is decrease in the cell voltage resulting from selfdischarging        after 16.7 hours                                                               **I is current density at tenth cycle of halfcell when cycled in 1 M           ZnSO.sub.4 (pH 2.3) between +0.35 V and +0.8 V at a scan rate of 20 mV/s;      ΔI is the decrease in current density after 100 cycles             

The polyaniline/organic dopant combination is useful as a battery electrode, in electrochromic displays and similar electrical applications where electrical conductivity is important.

While only a few embodiments of the invention have been shown and described herein, it will become apparent to those skilled in the art that various modifications and changes can be made in the use of a permanently doped water-insoluble polyaniline for use as a battery electrode and the method of manufacture without departing from the spirit and scope of the present invention. All such modifications and changes coming within the scope of the appended claims are intended to be carried out thereby. 

We claim:
 1. An electrically conducting water-insoluble polymer, said polymer having essentially permanent selfdoping properties as compared to a physical combination of polyaniline and an organic dopant having at least one sulfonic acid group, which polymer consists essentially of:(a) an electrically polymerized polyaniline which is chemically bonded to (b) an organic dopant, said dopant having at least one sulfonic acid functional group.
 2. The polymer of claim 1 wherein the organic dopant is an aliphatic organic sulfonic acid.
 3. The polymer of claim 2 wherein the organic dopant is selected from a saturated aliphatic organic compound having from 1 to 20 carbon atoms or is trifluoromethanesulfonic acid.
 4. The polymer of claim 1 wherein the organic-dopant is an aromatic organic sulfonic acid.
 5. The polymer of claim 4 wherein the aromatic sulfonic acid is selected from benzene sulfonic acid or a ring substituted benzene sulfonic acid.
 6. The electrically conducting polymer of claim 1 wherein the organic dopant is selected from benzenesulfonic acid, para-toluenesulfonic acid, benzenesulfonyl chloride, dodecylbenzenesulfonic acid, poly(vinylsulfonic) acid, methanesulfonic acid, trifluoromethanesulfonic acid, 1-butanesulfonic acid, modified perfluorsulfonic acid polymer, 2,3,5 trichlorobenzenesulfonic acid, vinylphenylsulfonic acid, or the alkali metal salts thereof.
 7. The electrically conducting polymer of claim 6 wherein the organic dopant is para- toluenesulfonic acid.
 8. The electrically conducting polymer of claim 6 wherein the organic dopant is trifluoromethanesulfonic acid.
 9. A method to produce a water-insoluble self-doped polyaniline polymer in which an organic dopant is chemically bonded to the polyaniline wherein the polymer-dopant combination has self-doping electrical properties as compared to a physical combination of polyaniline and an organic dopant having at least one sulfonic acid group, which method comprises:electropolymerizing a composition itself consisting essentially of(i) aniline in an aqueous solvent, and (ii) an organic dopant, said dopant having at least one organic sulfonic acid group.
 10. The method of claim 9 wherein the aromatic organic dopant is p-toluenesulfonic acid.
 11. The method of claim 9 wherein the organic dopant is trifluoromethanesulfonic acid.
 12. The method of claim 9 wherein in step (a) the electropolymerization occurs by cycling the voltage at between about -0.2 volt and +0.8 volt versus SCE.
 13. The method of claim 9 wherein the cycling has a sweep rate of about 100 millivolt per second.
 14. The method of claim 9 wherein the aqueous solution comprises between about 0.1 to 0.2 M of aniline and between about 0.8 and 1 M organic dopant.
 15. The method of claim 9 wherein the electropolymerization is performed at a pH of between about 0.65 and
 1. 16. The method of claim 9 wherein the scan rate is about 0.1 volt per second for between about 4 and 6 hours.
 17. The electrically conducting water-insoluble polyaniline having an organic dopant which is covalently bound to the polyaniline which is produced by the method of claim
 9. 18. The polyaniline polymer of claim 17 wherein the organic dopant is para-toluenesulfonic acid.
 19. The polyaniline polymer of claim 17 wherein the organic dopant is trifluoromethanesulfonic acid.
 20. The polyaniline polymer produced by the method of claim 9 wherein aniline is at a starting concentration of about 0.1 M, the organic dopant is p-toluenesulfonic acid at a starting concentration of about 1M, the voltage potential range is between about -0.1 and +0.9 V versus SCE, and the scan rate is about 0.1 V per second.
 21. The polyaniline polymer produced by the method of claim 9 wherein aniline is at a starting concentration of about 0.1 M, the organic dopant is trifluorosulfonic sulfonic acid at a concentration of about 1M, the voltage potential range is between about -0.2 and +0.9 V versus SCE, and the scan rate is about 0.1 V per second.
 22. The method of claim 9 wherein aniline is at a starting concentration of about 0.1M, the organic dopant is p-toluenesulfonic acid at a starting concentration of about 1M, the voltage potential range is between about -0.1 and +0.9 V versus SCE, and the scan rate is about 0.1V per second.
 23. The method of claim 9 wherein aniline is at a starting concentration of about 0.1M, the organic dopant is p-toluenesulfonic acid at a starting concentration of about 1M, the voltage potential range is between about -0.2 and +0.8 V versus SCE, and the scan rate is about 0.1 V per second.
 24. The method of claim 9 wherein the starting concentration of aniline is about 0.1M, the organic dopant is p-toluenesulfonic acid at a starting concentration of about 1 M, a voltage potential range is between about -0.2 and +0.8 volts versus SCE, and a scan rate of about 0.1 volt per second.
 25. The method of claim 9 having about a 0.1M starting concentration of aniline, a starting concentration organic dopant of 1M benzenesulfonic acid, a voltage potential range of between about -0.1 to +0.9 volts versus SCE, and a scan rate of about 0.1 volts per second.
 26. The method of claim 9 having an aniline at starting concentration of 0.1M, about a starting concentration of 12.5 percent by volume of an organic dopant of polyvinylsulfonic acid, a voltage potential range of between about -0.2 to +0.8 V (versus SCE) and a scan rate of about 0.1 V per second.
 27. The method of claim 9 having about a 0.1M starting concentration of aniline, a starting concentration of an organic dopant of 1M trifluoromethanesulfonic acid, a voltage potential range of about -0.1 to +0.9 versus SCE and a scan rate of 50.1 V per second. 